2c913 01 hobby aluminum casting co2 sand casting process Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting

Hobby Aluminum Casting | Sand Casting Aluminum | Green Sand Casting Process

CO2 Sand Casting process2c913 01 hobby aluminum casting co2 sand casting process Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting

CO2 sand casting or Hobby Aluminum casting is suitable for urgent and heavy orders with high accuracy and good surface finish on castings required. Hobby mould casters used this method because in this method elimination of core drying machine, but it is not an economical process. The only expense hobby mould caster encounters are the cost of the CO2 cylinder, regulator, and hoses and hand held applicator gun or nozzle. The operation is fast and the possibility of rejections is less. CO2 is a sand molding technique and it uses grain sand which is mixed with a solution of sodium silicate that acts as binding agent. CO2 gas is used to harden the mass of sand after the mould has been made. The chemical reaction takes place is explained below:

H2O + Na2SiO3 + CO2 à Na2CO3 + SiO2 (Silica Gel in Colloidal state)

Read More Info Regarding This Post :   Sand Casting | Metal Casting

In this process, CO2 gas is passed through sand mix (0.25% moisture content Sodium Silicate), then the sodium silicate sand becomes stiff gel which gives enough strength for the mould. Additives used are Coal powder, Wood Flour, Sea coal, Dextrin, Kaolin clay, Aluminium oxide and Invert Sugar.

Properties of Additives:

  1. Kaolin clay is used for mould stability
  2. Aluminium oxide is used for hot strength of bonded sand
  3. Invert Sugar is used after pouring to reduce the retained strength of the mould or core which removes from the mould with less shaking.

Steps involved

  1. Mould material is pure Silica, 3-5% of liquid base binder of sodium silicate, mulled for 3 to 4 minutes
  2. Now rammed around pattern in moulding box
  3. CO2 gas forced into mould at about 1.4 to 1.5 kg/cm2 for a predetermined time (15 to 30 seconds)
  4. Apply refractory coating, system ready for pouring
  5. Use either wood or metal pattern
  6. Suitable pressure reducing valves are used to reduce pressure of gas
  7. Pattern rubbed with graphite before ramming to overcome removal of pattern from mould
Read More Info Regarding This Post :   Pressure Thermite Welding | Thermite Welding Process

893f5 01 co2 gas mould sand casting process step 1 Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting

8b59e 01 co2 gas mould sand casting process step 2 runner and riser preparation Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting

f9a6d 01 co2 gas mould sand casting process step 3 vent holes Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting

6003a 01 co2 gas mould sand casting process step 4 supply carbon dioxide gas Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting

0d068 01 co2 gas mould sand casting process step 5 hardened mould surface Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting

Advantages:

  1. Low raw material cost
  2. Fast production rate
  3. No core or mould baking equipments
  4. Semi skilled workers enough
  5. Hollow moulds can be easily made
  6. Easily mechanized

Disadvantages:

  1. Difficult to reclaim the used sand
  2. Poor collapsibility due to inorganic nature of bond
  3. Moisture susceptibility
  4. Less suitable for non ferrous casting

Applications:

  1. For larger cores preparation
  2. Heavy or thick walled castings
  3. Producing cores of Fe, Al, Cu base alloys

6535e 01 metal casting hobby hobby molding Aluminum casting process Manufacturing Engineering Hobby Aluminum Casting